| 标准名称纤维增强水泥及其制品术语标准类型中华人民共和国国家标准标准号GB/T 16309-1996标准发布单位国家技术监督局标准正文 ……………………………………………662 mandrel ……………………………………………………………………………………664 mandrel loading and discharging device……………………………………………678 map cracking………………………………………………………………………………95 matrix………………………………………………………………………………………51 Mazza pipe machine………………………………………………………………………659 medium-alkali glass fiber………………………………………………………5222 mica……………………………………………………………………………………529 modulus of rupture………………………………………………………………………816 moisture content…………………………………………………………………………89 multiple cracking…………………………………………………………………………417 N natural ageing……………………………………………………………………………822 nominal asbestos-cement sheet…………………………………………………………922 nominal meter of asbestos-cement pipe………………………………………………921 non-alkali glass fiber……………………………………………………………5221 non-destructive test……………………………………………………………………914 O oil resistance……………………………………………………………………………828 one-dimentional aligned……………………………………………………………461 ordinary portland cement…………………………………………………………5112 orientation factor of fiber…………………………………………………………47 P paper making waste……………………………………………………………………539 paste……………………………………………………………………………………512 percentage of voids……………………………………………………………………86 pigment………………………………………………………………………………5311 pipe drawing……………………………………………………………………………635 plasticity………………………………………………………………………………413 pneumatic concentration of asbestos………………………………………………619 polypropylene fibrillated film fiber…………………………………………5232 polyvinyl alcohol fiber…………………………………………………………5231 pore structure……………………………………………………………………………85 portland cement……………………………………………………………………5111 precuring…………………………………………………………………………………637 precuring conveyor………………………………………………………………………679 premixing process………………………………………………………………………611 pressure drop………………………………………………………………………………912 pseudo-ductility…………………………………………………………………………419 pump-pulper…………………………………………………………………………………651 puncher………………………………………………………………………………………685 PVA fiber……………………………………………………………………………5231 PVA fiber cement………………………………………………………………………331 PVA fiber cement board………………………………………………………………735 Q quartz sand……………………………………………………………………………536 R reinforcement………………………………………………………………………………52 reinforcing efficiency of asbestos…………………………………………………410 resistence to chemical attack…………………………………………………………820 rinsing………………………………………………………………………………………628 rolling machine……………………………………………………………………………669 rubber ring…………………………………………………………………………5312 S sand cement…………………………………………………………………………5115 section modulus of asbestos-cement corrugated sheet…………………………920 semi-dry process……………………………………………………………………………62 seperating pipe from mandrel…………………………………………………………634 sepiolite…………………………………………………………………………………538 siliceous material…………………………………………………………………5116 single cracking……………………………………………………………………………416 single-piece hydraulic press……………………………………………………………677 slaked lime………………………………………………………………………………535 sleeve flexible joint…………………………………………………………………771 slurry concentration……………………………………………………………………623 slurry discharging………………………………………………………………………625 slurry making……………………………………………………………………………622 specific density…………………………………………………………………………82 spray coating set………………………………………………………………………686 spraying process…………………………………………………………………………68 spray-suction process……………………………………………………………………69 stack hydralic press……………………………………………………………………676 stacking machine for corrugated sheet……………………………………………671 steam curing………………………………………………………………………………640 steam-curing chamber……………………………………………………………………680 steel fiber…………………………………………………………………………527 steel wire……………………………………………………………………………527 stripping device………………………………………………………………………673 stripping of green sheet……………………………………………………………630 sulphate resiting portland cement…………………………………………5113 superposition of green sheet………………………………………………………631 surface coatings…………………………………………………………………5310 swelling…………………………………………………………………………………812 synthetic fiber……………………………………………………………………523 T template…………………………………………………………………………………643 template feeding machine……………………………………………………………672 texture index of asbestos……………………………………………………………618 texture of asbestos……………………………………………………………………617 thickness of asbestos-cement layer………………………………………………627 three-dimentional random orientation…………………………………………464 toughness…………………………………………………………………………………414 toughness index…………………………………………………………………………415 triaxile extruder pipe machine……………………………………………………661 tunnel curing room……………………………………………………………………681 turbine defibring machine……………………………………………………………650 two-dimentional aligned…………………………………………………………462 two-dimentional random orientation……………………………………………463 “#”type stacking…………………………………………………………………923 “≈”type stacking…………………………………………………………………924 U ultimate strength………………………………………………………………………813 V vacuum dewatering………………………………………………………………………633 vacuum formation machine………………………………………………………………667 vat…………………………………………………………………………………………657 voids ratio………………………………………………………………………………86 volume percentage of fiber……………………………………………………………48 W warping………………………………………………………………………………………825 waste dissolver……………………………………………………………………………658 water absorption…………………………………………………………………………810 water content………………………………………………………………………………89 water content of green sheet…………………………………………………………632 water glass………………………………………………………………………………532 water retentivity…………………………………………………………………………811 weatherability……………………………………………………………………………819 weathering resistance……………………………………………………………………819 wet process…………………………………………………………………………………61 winding process……………………………………………………………………………610 wire mesh………………………………………………………………………………5210 wire-mesh reinforced asbestos-cement sheet……………………………………723 wollastonite……………………………………………………………………………537 working pressure…………………………………………………………………………98 ____________________ 附加说明： 本标准由国家建筑材料工业局提出。 本标准由全国水泥制品标准化技术委员会归口。 本标准由国家建筑材料工业局苏州混凝土水泥制品研究院负责起草。 本标准主要起草人叶启汉、张明勇、韩静云。 本标准委托国家建筑材料工业局苏州混凝土水泥制品研究院负责解释。 |